Project Description
6063 6061 Extruded Aluminum T Slot Table For CNC Router
▹DESCRIPTION: 6000 Series T Slot Aluminum Profiles Table Anodising Silver For CNC Router
▹BRAND: FONNOV ALUMINIUM
▹APPLICATION: CNC Router, CNC Engraving Machine, Machinary, Industry Usage
▹PROFILE NO.: 20*80mm 20*240mm
▹QUALITY STANDARD: GB/T 6892-2015
▹ALUMINIUM ALLOY: 6063
▹TEMPER: T5
▹SURFACE TREATMENT: Anodized
▹FINISHING: smooth surface AA10
▹COLOUR: silver
▹LENGTH: As per request
▹PACKING METHOD: antistatic film & shrink film
▹PLACE OF ORIGIN: China
▹MOQ(MINIMIUM ORDER QUANTITY): /
▹NEAREST PORT: Qingdao Port & Shanghai Port as optional
▹STOCK OR NOT: stock is not available
OPTIONAL
▹ALUMINIUM ALLOY: 6063 | 6061
▹TEMPER: T5 | T6
▹SURFACE FINISHING: mill finish | powder coated | wood color | anodized | electrophoresis | PVDF
▹COLOUR: silver | bronze | champagne | gold | black anodising
▹PACKING METHOD: pearl cotton foam | craft paper | wooden pallet | metal pallet
▹APPLICATION: window | door | furniture, etc
EXTRA FABRICATION SERVICE
cut-to-length | hole punch | cnc milling | logo laser marking
Click FAQs For Commercial Terms and Technical Supports.
FOR PRODUCTION AND STOCK INFORMATION , PLEASE CONTACT US FOR DETAILS:
EMAIL: marketing@fonnov.com.cn | WECHAT: fonnov | WHATSAPP: +86 13395228957
6063 ALUMINUM
6063 aluminum alloy is a medium-strength heat-tremble strengthening alloy in AL-Mg-Si system. Mg and Si are the main alloying elements. It has excellent processing properties, excellent weldability, extrudability, and electroplating properties, and good Corrosion resistance, toughness, easy polishing, color film, excellent anodizing effect, is a typically extruded alloy.
6063 aluminum alloy is widely used in the construction of aluminum doors and windows, curtain wall frame, in order to ensure high wind pressure resistance, assembly performance, corrosion resistance and decorative performance of doors, windows and curtain walls, the comprehensive performance requirements of aluminum alloy profiles are much higher than industrial Profile standard. 6063 is the most common alloy used for aluminium extrusion. Applications requiring higher strength typically use 6061 or 6082 instead.
▹Chemical Component
| ALUMINIUM ALLOY | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Zr | OTHERS | AL | |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | —— | EACH | TOTAL | |
| 0.05 | 0.15 | REST | ||||||||||
▹Mechnical Properties
| Aluminium Alloy & Temper | Thickness | Tensile Strength | Yield Strength | Elongation /% | HBW |
| mm | Rm/Mpa | Rp0.2/Mpa | A | ||
| 6063-T5 | ≤3.00 | 175 | 130 | – | 65 |
| >3.00-25.00 | 160 | 110 | 7 | 65 | |
| 6063-T6 | ≤10.00 | 215 | 170 | – | 75 |
| >10.00-25.00 | 195 | 160 | 8 | 75 |
▹Physical Properties
| Aluminium Alloy & Temper | Thermal Coefficient of Expansion (20-100℃) μm/m·k Rm/Mpa | Melting Point (℃) Rp0.2/Mpa | Conductivity 20℃(68℉) (%IACS) | Resistivity 20℃(68℉) | Density (20℃)(g/cm3) Ωmm2/m |
| 6063 | 23.4 | 615-655 | 55-63 | 0.033 | 2.7 |
Colour Anodized Aluminum
PROCESS
Anodizing is an electro-chemical process, which physically alters the surface of the metal to produce a tough oxide layer on the surface.
It is mill finish aluminum before anodizing process, the anodizing production will be done in the tanks for the anodizing film, which can increases the thickness of the oxide coating on the aluminium improving its resistance to abrasion. The anodizing processes can be alkali etching and acid etching; also some extruders make the polishing, sand blasting or shot blasting operation on the aluminum profile before anodizing to remove the die line and scratch.
APPLICATIONS
Anodising is widely used in window and door, curtain wall, industrial profiles and decoration profiles.
COLOURS
The anodizing colors can be matt silver, anodized champagne, anodized bronze, anodized black, anodized gold and some other colors.
▹FILM THICKNESS
| Film Grade | Average / um ≥ | Local / um ≥ |
| AA10 | 10 | 8 |
| AA15 | 15 | 12 |
| AA20 | 20 | 16 |
| AA25 | 25 | 20 |
▹SEALING QUALITY ≤30mg/dm3
▹PROPERTIES
| Film Grade | Salt Spray Resistance | Abrasive Resistance | |
| Time /h | Grade | (f) g/um | |
| AA10 | 16 | ≥9 | ≥300 |
| AA15 | 24 | ≥9 | ≥300 |
| AA20 | 48 | ≥9 | ≥300 |
| AA25 | 48 | ≥9 | ≥300 |