Project Description
Aluminum Bathroom Cabinet
▹DESCRIPTION: Fully Aluminum Bathroom Cabinet
▹BRAND: FONNOV
▹APPLICATION: Bathroom
▹DESIGN NO.: FASF Series
▹ALUMINIUM ALLOY: 6063
▹TEMPER: T5
▹SURFACE TREATMENT: powder coating
▹COATING BRANDS: AKZO NOBEL(Netherland) / TIGER(Austria) or Chinese brands
▹FINISHING: matt gloss smooth surface
▹COLOUR: white, yellow, red, blue, and etc.
▹SIZE: custom as per drawing
▹PLACE OF ORIGIN: China
▹MOQ(MINIMIUM ORDER QUANTITY): 1SET
▹NEAREST PORT: Lianyungang Port ( Qingdao Port & Shanghai Port as optional)
▹STOCK OR NOT: stock is not available
OPTIONAL
▹SURFACE FINISHING: wood color | anodized | electrophoresis
▹COLOUR: red | white | black | blue | brown | grey, etc.
FOR PRODUCTION AND STOCK INFORMATION , PLEASE CONTACT US FOR DETAILS:
EMAIL: marketing@fonnov.com.cn | WECHAT: fonnov | WHATSAPP: +86 13395228957
6063 ALUMINUM
6063 aluminum alloy is a medium-strength heat-tremble strengthening alloy in AL-Mg-Si system. Mg and Si are the main alloying elements. It has excellent processing properties, excellent weldability, extrudability, and electroplating properties, and good Corrosion resistance, toughness, easy polishing, color film, excellent anodizing effect, is a typically extruded alloy.
6063 aluminum alloy is widely used in the construction of aluminum doors and windows, curtain wall frame, in order to ensure high wind pressure resistance, assembly performance, corrosion resistance and decorative performance of doors, windows and curtain walls, the comprehensive performance requirements of aluminum alloy profiles are much higher than industrial Profile standard. 6063 is the most common alloy used for aluminium extrusion. Applications requiring higher strength typically use 6061 or 6082 instead.
▹Chemical Component
| ALUMINIUM ALLOY | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Zr | OTHERS | AL | |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | —— | EACH | TOTAL | |
| 0.05 | 0.15 | REST | ||||||||||
▹Mechnical Properties
| Aluminium Alloy & Temper | Thickness | Tensile Strength | Yield Strength | Elongation /% | HBW |
| mm | Rm/Mpa | Rp0.2/Mpa | A | ||
| 6063-T5 | ≤3.00 | 175 | 130 | – | 65 |
| >3.00-25.00 | 160 | 110 | 7 | 65 | |
| 6063-T6 | ≤10.00 | 215 | 170 | – | 75 |
| >10.00-25.00 | 195 | 160 | 8 | 75 |
▹Physical Properties
| Aluminium Alloy & Temper | Thermal Coefficient of Expansion (20-100℃) μm/m·k Rm/Mpa |
Melting Point (℃) Rp0.2/Mpa |
Conductivity 20℃(68℉) (%IACS) |
Resistivity
20℃(68℉) |
Density (20℃)(g/cm3) Ωmm2/m |
| 6063 | 23.4 | 615-655 | 55-63 | 0.033 | 2.7 |
Powder Coated Aluminum
PROCESS
The powder coating process of powder coated aluminum starts with the metal components being cleaned, which helps the powder coating to adhere to the metal. This process is carried out in a multistage immersion water tank system as follows:
- A de-greaser and light etch is used to clean the metal after which a two bath rinse cleans it down.
- Next a non chromate bonder is applied to help the powder adhere to the aluminium.
- Finally a drying oven is used to ensure no moisture is present when the items are powder coated.
The components are then suspended from a jig and passed through a spray booth where the powder is applied by spray guns. Once the powder coating has been applied it is passed through a curing oven where the particles melt and fuse together and adhere to the components surface. This produces a uniform, smooth, durable finish.
APPLICATION
Powder coated aluminum is widely used in window and door, curtain wall, industrial profiles and decoration profiles.
COLORS & FINISHINGS
Generally we cover all the standard RAL colours, as well as custom colors.
The main finish reflects the gloss level of the final product, usually being Gloss, Satin or Matt. There is also the choice between Flat finish and Metallic.
We use mainly epoxy/polyester for indoor use; polyester for common outdoor use; super durable polyester for use near sea and high building. These three types of powder cover most of our customer’s application requirements.
▹GLOSS
| GLOSS RANGE(%) 60° | Tolerance | |
| Matt | 3~30 | ±5 |
| Medium Gloss | 31~70 | ±7 |
| High Gloss | 71~100 | ±10 |
▹COLOUR
| COLOR | no color difference visually |
| ΔE≤1.5 |
▹COATING THICKNESS ≥ 40um
▹MECHANICAL PROPERTIES
| Indentation Hardness | ≥ 80 |
| Adhesive Force | 0 grade |
| Impact Resistance | no rupture or shedding of coating |
| Erichsen Cupping | 5mm |
| Flexing Endurance | 3mm |